Hybrid Hot Mirrors

The hybrid hot mirrors consist of metallic and dielectric materials. The transmission peaks at around 75% at 600nm and the IR rejection (>95%) extends out to the FAR infrared. This coating would be used when longwave length rejection is needed and the visible transmission is less important.

Reynard Corporation standard parameters apply:

Substrate Material: Fused Silica

Thickness: 2.3mm ±0.2mm

Surface Quality: 80-50 Scratch & Dig

Parallelism: < 3 Arc Minutes

Environmental: Per MIL-M-13508C

Hardness: Per MIL-M-13508C

Adhesion: Per MIL-M-13508C

Visit our product selector to choose a hybrid hot mirror based on your desired thickness, substrate material, and optical qualities.  If you still don’t find what you’re looking for then let us create it for you, we offer custom solutions for your unique applications. If you have questions, contact us by phone or email.  We’re glad to assist you.  Reynard Corporation’s optical engineers will also work with you on your custom quote.